Characteristics:
1. The water reducer from this material has good adaptability to cement, especially to the cement with water demand.
2. The production process for water reducer from this material is relatively simple, which makes it more suitable for small-scale concrete admixture enterprises.
3. The water reducing rate of the product (solid content 20-22%) from this material is amount to 30% under 1.1% concrete addition.
4. The early strength and 28 days' strength of the water reducer from this material have been increased dramatically, compressive strength ratio %: 1 Day >=180: 7 Days>=170; 28 Days >=150.
5. The water reducer from this material has high durability, can efficiently reduce the water/gel ratio, enhance durability, reduce shrinkage and creep.
6. The water reducer from this material has such advantages as less slump loss, good concrete fluidity maintenance, obvious sustained release effect, slump retaining rate is >=200.
7. The water reducer from this material is environment friendly, no chloride ion detected, comply with the ISO 14000 national environment management standard.
Quality Standard
1. Appearance: White or yellow flaky
2. Unsaturation mmol/e: >=0.38
3. Moisture: <=0.2%
4. Hydroxyl Value mgKOH/g: 23.5±2.0,
5. PH value (1% aqueous solution):5.0-7.0